碳纤维自焊接骨架结构的形成及其复合材料性能研究

报道了一种将短切碳纤维(CF)自发焊接成三维网络结构的新方法.研究发现,尼龙6(PA6)与CF具有较强的相互作用,SEM照片及储能模量高温平台表明,添加少量PA6能够在PS基体中形成耐高温的CFPA6自焊接骨架结构,PA6用量越多,高温储能模量越高,自焊接骨架结构强度越大.研究证明,这种自焊接骨架结构能够大幅度提高PS/CF复合体系的热变形温度,碳纤维具有优异的导电导热性能,碳纤维骨架结构能够降低导电临界浓度,增强面内导热系数.进一步分析表明,PA6在碳纤维表面定向聚集是一个动力学过程,CF-PA6自焊接骨架强度与PA6黏附率NPA6呈线性关系;扩大PA6与PS的黏度差,延长热压时间均有利于提高NPA6,进而大幅提高网络结构强度.     

Ag-BiVO_4复合光催化剂的制备及其可见光光催化机理的研究

BiVO4是一种优良的可见光光催化剂,但是低电荷分离效率和表面吸附性差能严重地制约了其光催化活性的提高.我们通过简单易行的一步水热法制备了银-钒酸铋复合光催化剂(Ag-BiVO4).通过XRD、EDS、XPS、SEM、DRS、PL和BET等手段对其结构和光化学性质进行了详细表征.结果表明,银以Ag和Ag2O的形态存在于催化剂表面.在可见光照射下(λ≥420nm),以染料罗丹明B(Rhodamine B,RhB)和无色小分子水杨酸(Salicylic acid,SA)为模型污染物,考察了Ag-BiVO4和BiVO4的光催化活性.结果表明:Ag的引入能有效提高BiVO4的可见光催化活性,当Ag掺杂量为1.44%时,其光催化效率最高.吸附实验表明Ag的存在极大地加强了RhB在光催化剂表面的吸附.进一步实验表明Ag2O和Ag的相互协同作用使Ag/Ag2O-BiVO4可见光催化活性得到显著提高,其中Ag2O因与BiVO4形成p-n型异质结对其催化活性起到主导作用.     

Dipolar Rotors Orderly Aligned in Mesoporous Fluorinated Organosilica Architectures

New mesoporous covalent frameworks, based on hybrid fluorinated organosilicas, were prepared to realize a periodic architecture of fast molecular rotors containing dynamic dipoles in their structure. The mobile elements, designed on the basis of fluorinated p‐divinylbenzene moieties, were integrated into the robust covalent structure through siloxane bonds, and showed not only the rapid dynamics of the aromatic rings (ca. 10⁸ Hz at 325 K), as detected by solid‐state NMR spectroscopy, but also a dielectric response typical of a fast dipole reorientation under the stimuli of an applied electric field. Furthermore, the mesochannels are open and accessible to diffusing in gas molecules, and rotor mobility could be individually regulated by I₂ vapors. The iodine enters the channels of the periodic structure and reacts with the pivotal double bonds of the divinyl‐fluoro‐phenylene rotors, affecting their motion and the dielectric properties.     

A Chemically Triggered and Thermally Switched Dielectric Constant Transition in a Metal Cyanide Based Crystal

A dielectric constant transition is chemically triggered and thermally switched in (HPy)₂[Na(H₂O)Co(CN)₆] ( 2 , HPy=pyridinium cation) by single‐crystal‐to‐single‐crystal transformation and structural phase transition, respectively. Upon dehydration, (HPy)₂[Na(H₂O)₂Co(CN)₆] ( 1 ) transforms to its semi‐hydrated form 2 , accompanying a transition from a low‐dielectric state to a high‐dielectric state, and vice versa. This dielectric switch is also realized by a structural phase transition in 2 that occurs between room‐ and low‐temperature phases, and which corresponds to high‐ and low‐dielectric states, respectively. The switching property is due to the variation in the environment surrounding the HPy cation, that is, the hydrogen‐bonding interactions and the crystal packing, which exert predominant influences on the dynamics of the cations that transit between the static and motional states.     

A Family of Molecular Sieves Containing Framework‐Bound Organic Structure‐Directing Agents

Organic structure‐directing agents (OSDAs), such as quaternary ammonium cations and amines, used in the synthesis of zeolites and related crystalline microporous oxides usually end up entrapped inside the void spaces of the crystallized inorganic host lattice. But none of them is known to form direct chemical bonds to the framework of these industrially important catalysts and adsorbents. We demonstrate that ECR‐40, currently regarded as a typical silicoaluminophosphate molecular sieve, constitutes instead a new family of inorganic‐organic hybrid networks in which the OSDAs are covalently bonded to the inorganic framework. ECR‐40 crystallization begins with the formation of an Al–OSDA complex in the liquid phase in which the Al is octahedrally coordinated. This unit is incorporated in the crystallizing ECR‐40. Subsequent removal of framework‐bound OSDAs generates Al‐O‐Al linkages in a fully tetrahedrally coordinated framework.     

Unconventional Magnetic and Resistive Hysteresis in an Iodine‐Bonded Molecular Conductor

Simultaneous manipulation of both spin and charge is a crucial issue in magnetic conductors. We report on a strong correlation between magnetism and conductivity in the iodine‐bonded molecular conductor (DIETSe)₂FeBr₂Cl₂ [DIETSe=diiodo(ethylenedithio)tetraselenafulvalene], which is the first molecular conductor showing a large hysteresis in both magnetic moment and magnetoresistance associated with a spin‐flop transition. Utilizing a mixed‐anion approach and iodine bonding interactions, we tailored a molecular conductor with random exchange interactions exhibiting unforeseen physical properties.     

Environmental effects on fibre reinforced polymeric composites: Evolving reasons and remarks on interfacial strength and stability

The interface between fibre and matrix of fibrous polymeric composites is most critical and decisive in maintaining sustainability, durability and also reliability of this potential material, but unfortunately a comprehensive conclusion is yet to meet the label of confidence for the engineering viability. Fiber reinforced polymer (FRP) composites are being accepted and also utilized as better and reliable alternative materials for repairing and/or replacing conventional materials, starting from tiny objects to mega structure in various engineering applications. The promise and potential of these materials are sometimes threatened in speedy replacement of conventional materials because of their inhomogeneities and inherent susceptibility to degradation due to moist and thermal environments. Environmental conditioning is traditionally believed to be a physical phenomenon but present literature has revealed that the interdiffusion between fiber and polymer matrix resin comprises of physical, chemical, mechanical, physico-chemical and mechano-chemical phenomena. The failure and fracture behavior at ambient conditions itself is a complex phenomenon till at present. The service conditions which are mostly hygrothermal in nature, along with a variation of applied loads make the mechanical behavior nearly unpredictable, far off from conclusions in evaluating the short term as well as long term durability and reliability of FRPs. It is essential to accurately simulate the initial and subsequent evolution process of this kind of damage phenomena, in order to explore the full potential of the mechanical properties of composite laminates. The present review has emphasized the need of complying scattered as well as limited literature on this front, and has focused on creating the urgency to highlight the importance of judicious uses of these materials with minimum safety factors with an aim to achieving lighter weight in enhancing specific properties.     

Selective Template Removal by Thermal Depolymerization to Obtain Mesostructured Molybdenum Oxycarbide

The carbon content of mesostructured organic‐inorganic hybrid material of a cylindrical block copolymer template of poly(2‐vinylpyridine)‐block‐poly(allyl methacrylate) (P2VP‐b‐PAMA) and ammonium paramolybdate (APM) could be reduced by thermal depolymerization. By calcination in vacuo at 320 °C the PAMA core can be completely removed while the remaining P2VP brush preserves the mesostructure. The P2VP‐APM composite can then be carburized in‐situ to MoO_xC_y in a second pyrolysis step without any additional carbon source but P2VP. The molybdenum oxycarbide nanotubes obtained, form hierarchically porous non‐woven structures, which were tested as catalyst in the decomposition of NH₃. They proved to be catalytically active at temperatures above 450 °C. The activation energy was estimated from an Arrhenius Plot to be 127 kJ · mol^–1.     

Experimental study on the fiber pull-out of composites using digital gradient sensing technique

A method to measure the stress field at the fiber tip in the fiber pull out test was proposed by using a digital gradient sensing technique. First, the principle of digital gradient sensing is introduced, and the non-contact optical system of digital gradient sensing developed. Then, a fiber reinforced composite model specimen, where a nail was inserted in epoxy resin to act as a fiber, was performed, and a pull out test was conducted on the specimen using the digital gradient sensing technique. Finally, the angular deflections contour at the fiber tip was obtained, and the stress intensity factor was extracted from the angular deflections. The results show that the stress intensity factor at the fiber tip extracted from the angular deflections agreed with the results calculated by the finite element method.     

Scaling effect on the tensile properties of [±45/0/±45/0/±45] Polypropylene/Twaron laminates

The effects of scaling on the mechanical response under tension of balanced nonsymmetrical laminates were investigated for a thermoplastic composite: Polypropylene reinforced with Twaron^® fibers. The composite baseline was an 8-ply laminate which consisted of unidirectional plies arranged in the sequence [±45/0/±45/0/±45]. The influence of specimen size on the tensile properties was studied for one (thickness), two (in-plane) and three (volume) dimensional scaling. The stress-strain curves suggested some variation in laminate behavior owing to the dimensional scaling; nevertheless, a further analysis with the classical lamination theory demonstrated that the observed effect was due to small variations in the fiber volume fraction of the laminates. It was concluded that the mechanical properties of these thermoplastic laminates do not exhibit scaling effects. The failure mechanism of the laminates was studied at macroscopic level; a scale effect of the fracture mechanism was observed.